標準試驗條件:        

● 電壓:upto1.5kV

● 溫度:85°C

● 測試時間:4hours(typical)

● 干燥條件下，不需要水

類型                          受壓                                                     恢復
PID-s正面                85°C，+1.5 kV                             85°C，-1.5 kV

PID-p背面             85°C，+1.5 kV，無照明 85°C，        暗儲存或光照

PID-c背面                   85°C，+1.5 kV， 照明                    不可恢復

層壓      150°C，20min

樣品尺寸   210×210mm

適用于 A   PERC,AL-BSF,IBC,PERC+,雙面PERC,p型和n型電池 功率要求 110/230 V AC, 50/60 Hz

資質(zhì)認證   根據(jù)ISO9001準則制造，符合CE標準

參考文獻： cells  (1)K. Sporleder, V. Naumann, J. Bauer, S. Richter, A. Hähnel, S. Großer, M. Turek, C. Hagendorf, Local corrosion of silicon as root cause for potential induced  degradation at the rear side of bifacial PERC solar cells. physica status solidi (RRL)–Rapid Research Letters. 2019, doi 10.1002/pssr.201900163

(2)V. Naumann, K. Ilse, M. Pander, J. Tröndle, K. Sporleder, C. Hagendorf, Influence of soiling and moisture ingress on long term PID susceptibility of photovoltaic

modules, AIP Conference Proceedings 2147, 090005 (2019).

(3)K. Sporleder, V. Naumann, J. Bauer, S. Richter, A. Hähnel, S. Großer, M. Turek, C. Hagendorf, Root cause analysis on corrosive potential-induced degradation effects  at the rear side of bifacial silicon PERC solar cells, Solar Energy Materials and Solar Cells 201, 110062 (2019).

(4)K. Sporleder, V. Naumann, J. Bauer, S. Richter, A. Hähnel, S. Großer, M. Turek, C. Hagendorf, Microstructural Analysis of Local Silicon Corrosion of Bifacial Solar Cells

as Root Cause of Potential‐Induced Degradation at the Rear Side, Phys. Status Solidi A (2019), doi:10.1002/pssa.201900334.

(5)K. Sporleder, J. Bauer, S. Großer, S. Richter, A. Hähnel, M. Turek, V. Naumann, K. Ilse, C. Hagendorf, Potential-Induced Degradation of Bifacial PERC Solar Cells Under  Illumination, IEEE Journal of Photovoltaics 9 (6) 1522-1525, 2019.

(6)K. Sporleder, M. Turek, N. Schüler, V. Naumann, D. Hevisov, C. Pöblau, S. Großer, H. Schulte-Huxel, J. Bauer, C. Hagendorf, Quick test for reversible and irreversible  PID of bifacial PERC solar cells, Solar Energy Materials and Solar Cells 219, 110755, 2021.

(7)K. Sporleder, V. Naumann, J. Bauer, D. Hevisov, M. Turek, and C. Hagendorf, Time-resolved Investigation of Transient Field Effect Passivation States during Potential  Induced Degradation and Recovery of Bifacial Silicon Solar Cells , Solar RRL, 2021, accepted.